Mechanisms for forming hybrid bonding structures with elongated bumps

ABSTRACT

Embodiments of mechanisms for forming a package structure are provided. The package structure includes a semiconductor die and a substrate. The package structure includes a pillar bump and an elongated solder bump bonded to the semiconductor die and the substrate. A height of the elongated solder bump is substantially equal to a height of the pillar bump. The elongated solder bump has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of the elongated solder bump, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface. A ratio of the second width to the first width is in a range from about 0.5 to about 1.1.

BACKGROUND

The fabrication of modern integrated circuits (ICs) involves several process steps. Integrated circuits are first fabricated on/in a semiconductor wafer. The semiconductor wafer contains multiple duplicated semiconductor chips, each including integrated circuits. The semiconductor chips are then sawed from the semiconductor wafer and packaged. The packaging process has two main purposes: to protect delicate semiconductor chips, and to connect interior integrated circuits to exterior connections.

As semiconductor devices reach higher levels of integration, the packaging of a semiconductor chip accounts for a considerable portion of the cost of producing the device. Failure of the package leads to costly yield reduction.

There are challenges in fabricating reliable package structures.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompany drawings, in which:

FIG. 1A shows a cross-sectional view of a package structure, in accordance with some embodiments.

FIG. 1B shows an enlarged cross-sectional view of a portion of the package structure shown in FIG. 1A, in accordance with some embodiments.

FIGS. 2A-2B are cross-sectional views before and after a package structure is formed, in accordance with some embodiments.

FIG. 3 shows a cross-sectional view of elongated solder bumps, in accordance with some embodiments.

FIG. 4 shows an enlarged cross-sectional view of a portion of the package structure shown in FIG. 2B, in accordance with some embodiments.

FIGS. 5A-5G are cross-sectional views at various stages of a process for forming a package structure, in accordance with some embodiments.

FIGS. 6A-6B are cross-sectional views of applying flux and placing a solder material ball, in accordance with some embodiments.

FIGS. 7A-7D are top views showing various arrangements of pillar bumps and elongated solder bumps of bonding structures, in accordance with some embodiments.

FIG. 8 shows a cross-sectional view of a package structure, in accordance with some embodiments.

FIG. 9 shows a cross-sectional view of a package structure, in accordance with some embodiments.

DETAILED DESCRIPTION OF THE ILLUSTRATIVE EMBODIMENTS

The making and using of the embodiments of the disclosure are discussed in detail below. It should be appreciated, however, that the embodiments can be embodied in a wide variety of specific contexts. The specific embodiments discussed are merely illustrative, and do not limit the scope of the disclosure.

It is to be understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the disclosure. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. Moreover, the performance of a first process before a second process in the description that follows may include embodiments in which the second process is performed immediately after the first process, and may also include embodiments in which additional processes may be performed between the first and second processes. Various features may be arbitrarily drawn in different scales for the sake of simplicity and clarity. Furthermore, the formation of a first feature over or on a second feature in the description that follows include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact.

Some variations of the embodiments are described. Throughout the various views and illustrative embodiments, like reference numbers are used to designate like elements.

FIG. 1A is a cross-sectional view of a package structure 180 formed by bonding a semiconductor die 100 and a substrate 106, in accordance with some embodiments. Semiconductor die 100 is flipped upside down and attached to a substrate 106 through bonding structures 150. In some embodiments, semiconductor die 100 is made of an elementary semiconductor material including silicon or germanium in a single crystal, polycrystal, or amorphous structure. In some other embodiments, semiconductor die 100 is made of a compound semiconductor, such as silicon carbide, gallium arsenide, gallium phosphide, indium phosphide, indium arsenide, an alloy semiconductor, such as SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, GaInAsP, and/or combinations thereof. In some embodiments, semiconductor die 100 includes silicon on insulator (“SOI”). In some embodiments, semiconductor die 100 also includes passive devices such as resistors, capacitors, inductors and the like, or active devices such as transistors. In some embodiments, semiconductor die 100 may include through substrate vias (TSVs).

Semiconductor die 100 may further include isolation features (not shown), such as shallow trench isolation (STI) features or local oxidation of silicon (LOCOS) features. The isolation features may define and isolate various device elements. Examples of the various device elements, that may be formed in semiconductor die 100, include transistors (e.g., metal oxide semiconductor field effect transistors (MOSFET), complementary metal oxide semiconductor (CMOS) transistors, bipolar junction transistors (BJT), high voltage transistors, high frequency transistors, p-channel and/or n channel field effect transistors (PFETs/NFETs), etc.), diodes, and/or other suitable elements. Various processes are performed to form the various device elements, such as deposition, etching, implantation, photolithography, annealing, and/or other suitable processes.

Substrate 106 may be made of any applicable type of substrate materials, such as a package susbtrate, a print circuit board (PCB) substrate, or the materials used for semiconductor die 100. In some embodiments, substrate 106 also includes passive devices, such as resistors, capacitors, inductors and the like, or active devices, such as transistors. In some embodiments, substrate 106 includes additional integrated circuits. Substrate 106 may further include through substrate vias (TSVs) and may be an interposer.

Each of bonding structures 150 includes a pad 101, an under bump metallurgy (UBM) layer 102, a solder bump 104, and a pad 108. UBM layer 102 is formed over pads 101 on semiconductor die 100. Pads 108 are formed over substrate 106. Pads 101 and 108 are conductive and electrically connected to devices formed in semicodncutor die 100 and substrate 106, respectively. Pads 101 and 108 may be made of aluminum, copper, gold, titanium, platinum, another suitable material, alloy thereof, or combinations thereof. In some embodiments, UBM layer 102 includes sub-layers. For example, UBM layer 102 includes a Ti sub-layer and a Cu sub-layer. The Cu sub-layer may serve as a Cu seed layer which is made of Cu or Cu alloy. Solder bumps 104 are formed between UBM layer 102 and pads 108. Solder bumps 104 may include lead or lead free materials.

In some embodiments, bonding structures 150 include structures 150M, which are away from corners of semiconductor die 100, and corner structures 150C. After a thermal cycling of bonding processes, high stress is generated on corner structures 150C due to mismatch of CTE (coefficients of thermal expansion) between semiconductor die 100 and substrate 106. For example, the high stress may concentrate at regions R of corner structures 150C. Such high stress could result in bump cracking and reduce the yield of package structure 180.

FIG. 1B is an enlarged cross-sectional view of a portion of package structure 180 shown in FIG. 1A, in accordance with some embodiments. Solder bump 104 has a sidewall surface 105 curved outwardly. Solder bump 104 has a width W₁ at a horizontal plane P₁ passing through an upper end E of sidewall surface 105. In addition, solder bump 104 has a second width W₂ at a horizontal plane P₂ passing through a midpoint M of sidewall surface 105. A ratio of width W₂ to width W₁ is in a range from about 1.1 to about 1.4. An angle θ₁ between horizontal plane P₁ passing through upper end E and a tangent line T₁ of sidewall surface 105 passing through upper end E may be in a range from about 110 degrees to about 140 degrees.

As mentioned above, region R of corner structure 150C, near an interface between a corner solder bump 104 and UBM layer 102, suffers from high stress. According to a stress simulation, portion 104H of solder bump 104 in region R (see FIG. 1A) suffers from the highest stress after a thermal cycling. In contrast, portion 104L of solder bumps 104 at the widest portion of solder bump 104 has less stress than portion 104H. The highly concentrated stress at portion 104H of solder bump 104 could result in bump cracking near or at interface between solder bump 104 and UBM layer 102.

Simulation result shows that the stress in elongated solder bumps is redistributed. Therefore, the corner regions of the elongated solder bumps suffer from less stress than regular solder bumps 104. Therefore, it is desirable to form bonding structures with elongated solder bumps to reduce high stress in corner regions.

FIGS. 2A-2B are cross-sectional views before and after a package structure 280 is formed, in accordance with some embodiments. FIG. 2A shows semiconductor die 100 and substrate 106 before they are bonded, in accordance with some embodiments. Pads 101 and UBM layer 102 have been described above.

In some embodiments, conductive elements 204 are formed on UBM layer 102. Conductive elements 204 are made of a metal material, such as copper (Cu), gold (Au), platinum (Pt), titanium (Ti), nickel (Ni), or combinations thereof, in accordance with some embodiments. Conductive elements 204 may be formed by using an electroplating process, PVD process, another applicable process, or combinations thereof. Each of conductive elements 204 has a substantially flat surface. In some embodiments, conductive elements 204 are conformally deposited on UBM layer 102. In some embodimenhts, conductive elements 204 are made of solder.

Conductive pillars 206 are formed on some of conductive elements 204. Conductive pillar 206 may be made of a metal material, such as copper (Cu), gold (Au), platinum (Pt), titanium (Ti), nickek (Ni), aluminum (Al) or combinations thereof. Conductive pillars 206 have sidewalls 207 substantially perpendicular to a main surface 100 a of semiconductor die 100.

In some embodiments, solder balls 114 are bonded to remaining conductive elements 204 where no conductive pillars 206 are formed. Conductive pillars 206 have a higher melting temperature than that of solder balls 114. Solder balls 114 have a height H₁ which is substantially equal to a height H₂ of conductive pillars 206. In some embodiments, height H₂ of conductive pillars 206 may be in a range from about 130 μm to about 250 μm. In some other embodiments, height H₂ of conductive pillars 206 may be in a range from about 150 μm to about 190 μm. A solder layer 208 is provided on pads 108 for bonding with solder balls 114 and conductive pillars 206.

Semiconductor die 100 is positioned over substrate 106 to align solder balls 114 and conductive pillars 206 with solder layer 208 on pads 108, respectively. Afterwards, semiconductor die 100 and substrate 106 are placed against each other with applying a pressure to them. A reflow process is also performed to bond solder balls 114 with solder layer 208 and to bond conductive pillars 206 with solder layer 208, as shown in FIG. 2B. After the reflow process, elongated solder bumps 104′ and pillar bumps 210 are obtained. Each of pillar bumps 210 includes conductive pillar 206 and solder layer 208. Semiconductor die 100 and substrate 106 are bonded to each other through elongated solder bumps 104′ and pillar bumps 210. In some embodiments, a ratio of the number of elongated solder bumps 104′ to the number of pillar bumps 210 is in a range from about 20% to about 75%.

Package structure 280 with hybrid bonding structures 250 is therefore formed. Hybrid bonding structures 250 include structures 250M having pillar bumps 210 and corner structures 250C having elongated solder bumps 104′. Specifically, each of structures 250M includes pad 101, UBM layer 102, conductive element 204, pillar bump 210, solder layer 208, and pad 108. Each of corner structures 250C includes pad 101, UBM layer 102, a conductive element 204, elongated solder bump 104′ and a pad 108.

During the reflow for forming elongated solder bump 104′ and pillar bumps 210, conductive pillars 206 remain rigid and help to maintain a height H₃ between semiconductor die 100 and substrate 106. Therefore, solder balls 114 and solder layer 208 are reflowed between conductive element 204 and pads 108 without being further pressed. As a result, solder bump 104′ is elongated. Sidewall surfaces 207 of conductive pillars 206 are still substantially perpendicular to main surface 100 a of substrate 100 after forming pillar bumps 210.

In some embodiments, elongated solder bumps 104′ only protrude outward slightly after the thermal reflow when compared to solder bumps 104 shown in FIGS. 1A and 1B. Elongated solder bumps 104′ have slightly bulged sidewall surfaces 105′. In some embodiments, sidewall surfaces 105′ are almost parallel with sidewall surfaces 207 of conductive pillars 206. Height H₁ is substantially equal to height H₂, which ensures that both solder balls 114 and conductive pillar 206 are in contact with solder layer 208. Since height H₃ between semiconductor die 100 and substrate 106 is maintained, pillar bumps 210 and elongated solder bumps 104′, which are formed therebetween, thus have substantially the same height.

Regions R₁ are near an interface between elongated corner solder bump 104′ and conductive element 102. Simulation confirms that less stress are concentrated at regions R₁, compared with regions R shown in FIG. 1A. The stress in elongated solder bumps 104′ is redistributed after the thermal reflow, and the stress in regions R₁ is much reduced. The bump cracking risk is reduced.

As shown in FIG. 2B, sidewall surfaces 105′ of elongated solder bump 104′ protrude outward slightly. However, it should be appreciated that embodiments of the disclosure are not limited to the structure shown in FIG. 2B. Elongated solder bumps 104′ may have a cross-sectional view with other shapes. For example, elongated solder bumps 104′ may have straight sidewall surfaces 205′ or contracted sidewall surfaces 305′ (i.e., curved inward), as shown in FIG. 3.

FIG. 4 shows an enlarged view of a portion of package structure 280 shown in FIG. 2B, in accordance with some embodiments. Elongated solder bump 104′ has a width W₁ at a horizontal plane P₁′ parallel to main surface 100 a and passing through an upper end E′ of a sidewall surface 105′ of elongated bump 104′. Elongated solder bump 104′ has a second width W₂′ at a horizontal plane P₂′ passing through a midpoint M′ of sidewall surface 105′. In some embodiments, a ratio of width W₂′ to width W₁ is in a range from about 0.5 to about 1.1. In some other embodiments, the ratio of width W₂′ to width W₁ is in a range from about 0.8 to about 1.1. An angle θ₂ between horizontal plane P₁′ passing through upper end E′ of sidewall surface 105′ and a tangent line T₂ of sidewall surface 105′ passing through upper end E′ is smaller than angle θ₁ as shown in FIG. 1B. For example, angle θ₂ may be in a range from about 60 degrees to about 100 degrees. In some other embodiments, angle θ₂ may be in a range from about 80 degrees to about 95 degrees.

Embodiments of the disclosure may be formed by using a variety of processes. FIGS. 5A-5G are cross-sectional views at various stages of a process for forming a package structure, in accordance with some embodiments. As shown in FIG. 5A, semiconductor die 100 is provided. Semiconductor die 100 includes a region A₁, where an elongated bump will be formed, and a region A₂, where a conductive pillar will be formed. Pads 101 a and 101 b are formed over regions A₁ and A₂, respectively. Pads 101 a and 101 b are similar to pads 101. An interconnection structure 302 including dielectric layers and metal layers is formed between semiconductor die 100 and pads 101 a and 101 b. The metal layers of interconnection structure 302 provide electrical connections between the device elements formed in semiconductor die 100 and pads 101 a and 101 b.

One or more passivation layers, such as a passivation layer 306, is/are deposited and patterned over interconnection structure 302 and pads 101 a and 101 b. Passivation layer 306 has openings exposing pads 101 a and 101 b. In some embodiments, passivation layer 306 is made of a dielectric material, such as a polymer material. The polymer material may be made of polybenzoxazole (PBO), epoxy, polyimide, another suitable material, or combinations thereof. Passivation layer 306 may be deposited by any suitable method, such as a spin-on process, CVD process, another suitable process, or combinations thereof.

Afterwards, as shown in FIG. 5B, a UBM layer 102 is conformally formed over pads 101 a and 10 ab and passivation layer 306. UBM layer 102 is described above. Afterwards, a mask layer 308 is deposited and patterned over UBM layer 102. Mask layer 308 has openings exposing UBM layer 102 over pads 101 a and 101 b. Mask layer 308 may be a photoresist layer. A thickness t₁ of mask layer 308 may be in a range from about 7 μm to about 120 μm.

Afterwards, conductive element 204 a is formed in the opening of mask layer 308 over region A₁ and a conductive element 204 b is formed in opening of mask layer 308 over region A₂. In some embodiments, conductive elements 204 a and 204 b may completely fill the openings of mask layer 308. Alternatively, conductive elements 204 a and 204 b may partially fill openings of mask layer 308. Conductive elements 204 a and 204 b may be made of a metal material, such as copper (Cu), gold (Au), platinum (Pt), titanium (Ti), nickek (Ni), aluminum (Al), or combinations thereof.

In some embodiments, conductive elements 204 a and 204 b are directly deposited on the seed layer of UBM layer 102 by plating, such as electroplating. In some other embodiments, conductive element 204 a and 204 b are formed by other depositing methods, such as PVD. Afterwards, the portions of conductive elements 204 a and 204 b outside the openings are removed by a CMP process to planarize conductive elements 204 a and 204 b. Each of conductive elements 204 a and 204 b has a flat upper surface.

Aternatively, in some embodiments, conductive elements 204 a and 204 b are conformally deposited on UBM layer 102. Each of conductive elements 204 a and 204 b has a recessed upper surface. In some other embodiments, conductive elements 204 a and 204 b are not needed.

Afterwards, as shown in FIG. 5C, a mask layer 310 is deposited and patterned over mask layer 308. Mask layer 310 has an opening exposing conductive element 204 b over region A₂. Conductive element 204 a is covered by mask layer 310. Mask layer 310 may be a photoresist layer. A thickness t₂ of mask layer 310 may be in a range from about 90 μm to about 130 μm. Usually, mask layer 310 is thicker than mask layer 308. In some embodiments, a dry photosensitive film is used as mask layer 310.

Afterwards, conductive pillar 206 is formed over conductive element 204 b in the opening of mask layer 310. In some embodiments, conductive pillar 206 is formed on conductive element 204 b. In some embodiments, sidewalls surfaces of the opening of mask layer 310 are substantially perpendicular to surface 100 a of semiconductor die 100. Therefore, conductive pillar 206 has sidewall surfaces 207 substantially perpendicular to surface 100 a of semiconductor die 100. In some other embodiments, pillar 206 is formed by using a plating process, a PVD process, another applicable process, or combinations thereof. In some embodiments, conductive pillar 206 and conductive element 204 b are formed of the same material, and conductive element 204 b is construed as an extension of conductive pillar 206.

A total thickness (t₁+t₂) of mask layers 308 and 310 may be in a range from about 120 μm to about 250 μm. The total thickness of mask layers 308 and 310 may be set to be similar to the desired height of conductive pillar 206. Therefore, the height of conductive pillar 206 may be adjusted by tuning the total thickness of mask layers 308 and 310.

As shown in FIG. 5D, mask layers 310 and 308 are then removed by using a stripping process, in accordance with some embodiments. In addition, exposed portions of UBM layer 102 is removed by using, for example, an etching process.

Following the etching process removing the exposed portions of UBM layer 102, a flux stencil 312 is then provided and positioned above semiconductor die 100, in some embodiments. Flux stencil 312 may have openings 314. Openings 314 are aligned with conductive element 204 a in region A₁ and conductive pillar 206 in region A₂, respectively. Each of openings 314 may have a width which is smaller than that of conductive element 204 a or that of conductive pillar 206.

Flux 316 is then applied on conductive element 204 a and conductive pillar 206 through openings 314 of flux stencil 312. A flux material may be blanketly applied on flux stencil 312. The flux material penetrates through openings 314 to form flux 316 on surfaces of conductive element 204 a and conductive pillar 206. Flux 316 over conductive element 204 a and conductive pillar 206 are simultaneously formed. Afterwards, flux stencil 312 is removed.

After flux 316 is applied, a bump placing stencil 318 is provided and positioned above semiconductor die 100 to help the alignment of placing solder balls, as shown in FIG. 5E. Bump placing stencil 318 has an opening 320. Opening 320 is aligned with flux 316 over conductive element 204 a. Opening 320 has a width larger than that of conductive element 204 a.

A solder material ball 514 is placed over conductive element 204 a. In some embodiments, solder material ball 514 lands on flux 316, which is on conductive element 204 a, through opening 320 of bump placing stencil 318. Solder material ball 514 is secured over conductive element 204 a by flux 316. Afterwards, bump placing stencil 318 is removed.

Afterwards, as shown in FIG. 5F, a thermal reflow is performed to bond solder material ball 514 to conductive element 204 a to form solder ball 114. Flux 316 evaporates due to the thermal reflow. Substrate 106 is then provided to bond with semiconductor die 100. Pads 108 are formed over substrate 106. Solder layer 208 is applied on pads 108 to bond with solder ball 114 and conductive pillar 206. Semiconductor die 100 is positioned over and aligned with substrate 106 for bonding.

As shown in FIG. 5G, semiconductor die 100 is then bonded with substrate 106 by reflow, in accordance with some embodiments. As mentioned above, the existence of conductive pillar 206 enables the formations of elongated solder bump 104′. In addition, conductive pillar 206 is bonded to solder layer 208 to form pillar bump 210. Package structure 280 with hybrid bonding structures 250 is therefore formed. Hybrid bonding structures 250 include a corner structure 250C having elongated solder bumps 104′ and a structure 250M having pillar bump 210. Since the stress is redistributed in elongated solder bump 104′, the stress at corner regions R₁ is reduced. Elongated solder bump 104′ suffers from less stress at corner regions R₁, compared with corner regions R of solder bump 104 shown in FIG. 1A. As a result, bump cracking risk is significantly reduced, and yield of package structure 280 is greatly improved.

Alternatively, flux 316 and solder material ball 514 are applied on conductive elements 204 a and 204 b with different stencils. FIGS. 6A-6B are cross-sectional views of applying flux 316 and placing solder material ball 514, in accordance with some embodiments. As shown in FIG. 6A, conductive pillar 206 is formed, and then mask layers 310 and 308 and the exposed UBM layer 102 are removed. Afterwards, a flux stencil 412 is provided and positioned above semiconductor die 100. Flux stencil 412 may have an opening 414 aligned with and exposing conductive element 204 a. Opening 414 may have a width smaller than that of conductive element 204 a.

Flux stencil 412 also has a cavity 413 aligned with conductive pillar 206. After flux stencil 412 is put on semiconductor die 100, conductive pillar 206 is within cavity 413 and covered by flux stencil 412. Cavity 413 has a width larger than that of conductive pillar 206. Then, flux material is applied on flux stencil 412. The flux material penetrates through opening 414 of flux stencil 412 to reach conductive element 204 a. Flux stencil 412 protects conductive pillar 206 from being contacted with the flux material. Afterwards, flux stencil 412 is removed, and the flux material is spread over conductive element 204 a to form flux 316, as shown in FIG. 6B.

Afterwards, a bump placing stencil 418 is provided and positioned above semiconductor die 100, as shown in FIG. 6B. Bump placing stencil 418 has an opening 420. Opening 420 is aligned with and exposes flux 316 over conductive element 204 a. Opening 420 has a width larger than that of conductive element 204 a. Solder material ball 514 is placed on flux 316 through opening 420. Afterwards, bump placing stencil 418 is removed. The process operations described in FIGS. 5F-5G are performed. Afterwards, package structure 280 is formed as shown in FIG. 5G.

Package structure 280 has many hybrid bonding structures 250 including corner structures 250C and structures 250M. FIGS. 7A-7D are top views showing various arrangements of pillar bumps 210 and elongated solder bumps 104′ of bonding structures 250.

In some embodiments, elongated solder bumps 104′ and pillar bumps 210 are formed on different regions of semiconductor die 100. As shown in FIG. 7A, elongated solder bumps 104′ are formed on corner regions RE₁ of semiconductor die 100. Pillar bumps 210 are formed on the remaining region of semiconductor die 100 to assist in the formation of elongated solder bumps 104′. In some embodiments, after a thermal cycling, corner regions RE₁ suffer from higher stress than the remaining regions due to mismatch of the CTE of semiconductor die 100 and the substrate after reflow. The formation of elongated solder bumps 104′ on corner regions RE₁ reduces bump cracking risk and improves reliability of package structure 280. In some embodiments, a side of semiconductor die 100 has a width D. Each of corner regions RE₁ has a smaller width which is equal to D/n, and n is a number, which is in a range from about 3 to about 8.

As shown in FIG. 7B, elongated solder bumps 104′ may also be formed on a central portion RE₂ of semiconductor die 100. The formation of elongated solder bumps 104′ on central portion RE₂ provides support when package structure 280 drops from height or suffers from collision.

It should be appreciated that the arrangements of elongated solder bumps 104′ and pillar bumps 210 are not limited to those shown in FIGS. 7A and 7B. For example, other arrangements of elongated solder bumps 104′ and conductive pillars 206 are shown in FIGS. 7C and 7D. As shown in FIG. 7C, in some embodiments, pillar bumps 210 are on corner regions RE₁. No solder bump or pillar bump formed on central region RE₂. Elongated solder bumps 104′ are formed on the remaining region. Accordingly, additional buffer may be provided for the package structure. As shown in FIG. 7D, in some embodiments, pillar bumps 210 are formed on both corner regions RE₁ and central region RE₂ to meet other design requirements.

FIG. 8 is a cross-sectional views a package structure 380, in accordance with some embodiments. Pillar bumps 810 are made of the same materials with pillar bumps 210 mentioned above. Pillar bumps 810 and elongated solder bumps 804′ are directly formed on UBM layer 102. Therefore, the upper surfaces of pillar bumps 810 and elongated solder bumps 804′ are not flat and are conformal with the shape of UBM layer 102.

FIG. 9 is a cross-sectional views a package structure 480, in accordance with some embodiments. As shown in FIG. 9, pillar bumps 910 other than pillar bumps 210 or 810 mentioned above are formed over semiconductor die 100. Pillar bumps 910 include pillars 906 and a bonding layer 908. Pillars 906 have sidewall surfaces 907. Sidewall surfaces 907 may be substantially perpendicular to main surface 100 a of semiconductor die 100. Alternatively, sidewall surfaces 907 may not be perpendicular to main surface 100 a of semiconductor die 100.

Pillars 906 may be made of an insulating material, semiconductor material, metal material, other suitable material, or combinations thereof. Pillars 906 have a melting point (or a softing point) higher than solders. In some embodiments, pillar bumps 910 are not formed over a UBM layer when they are not electrically connected to devices formed in semiconductor die 100. In some embodiments, bonding layer 908 is a solder layer or an adhesive layer. For example, bonding layer 908 may be an adhesive layer when pillars 906 are made of insulating materials or semiconductor materials. In some embodiments, the adhesive layer includes glues, resins, other applicable materials, solder paste, flux, or combinations thereof.

Embodiments of mechanisms for bonding a semiconductor die to a substrate are described. A distance between the semiconductor die and the substrate, during and after a reflow process, is sustained by pillars whose melting temperature is higher than solder. Due to the rigid pillars, solder bumps between the semiconductor die and the substrate are elongated after reflow. The elongated solder bumps have less stress at corner regions than regular solder bumps. As a result, cracking risk of the elongated solder bumps is significantly reduced, and the reliability of the package structure is greatly improved. The hybrid bonding structures between the semiconductor die and the substrate include hybrid mixture of pillar bumps and elongated solder bumps.

In accordance with some embodiments, a package structure is provided. The package structure includes a semiconductor die and a substrate. The package structure includes a pillar bump and an elongated solder bump bonded to the semiconductor die and the substrate. A height of the elongated solder bump is substantially equal to a height of the pillar bump. The elongated solder bump has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of the elongated solder bump, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface. A ratio of the second width to the first width is in a range from about 0.5 to about 1.1.

In accordance with some embodiments, a package structure is provided. The package structure includes a semiconductor die and a substrate. The package structure also includes a plurality of pillar bumps and a plurality elongated solder bumps bonded to the semiconductor die and the substrate. A height of each of the elongated solder bumps is substantially equal to a height of each of the pillars. Each of the elongated solder bumps has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of the elongated solder bump, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface. A ratio of the second width to the first width is in a range from about 0.5 to about 1.1.

In accordance with some embodiments, a method for forming a package structure is provided. The method includes providing a semiconductor die and forming a pillar and a solder ball over the semiconductor die. The pillar has a melting point higher than that of the solder ball. The method also includes bonding the pillar and the solder ball to a substrate through a reflow process with forming a pillar bump and an elongated solder bump. A height of the elongated solder bump is substantially equal to a height of the pillar bump. The elongated solder bump has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of the elongated solder bump, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface. A ratio of the second width to the first width is in a range from about 0.5 to about 1.1.

Although the embodiments and their advantages have been described in detail, it should be understood that various changes, substitutions, and alterations can be made herein without departing from the spirit and scope of the embodiments as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, composition of matter, means, methods, and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. In addition, each claim constitutes a separate embodiment, and the combination of various claims and embodiments are within the scope of the disclosure. 

1. A package structure, comprising: a semiconductor die; a substrate; a pillar bump bonded to the semiconductor die and the substrate; and an elongated solder bump bonded to the semiconductor die and the substrate, wherein a height of the elongated solder bump is substantially equal to a height of the pillar bump, wherein the elongated solder bump has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of the elongated solder bump, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface, and wherein a ratio of the second width to the first width is in a range from about 0.5 to about 1.1.
 2. The package structure as claimed in claim 1, wherein the pillar bump comprises a pillar and a bonding layer.
 3. The package structure as claimed in claim 2, wherein the pillar is a conductive pillar.
 4. The package structure as claimed in claim 2, wherein the pillar has a melting point higher than that of the elongated solder bump.
 5. The package structure as claimed in claim 2, wherein the pillar has a sidewall surface substantially perpendicular to a main surface of the semiconductor die.
 6. The package structure as claimed in claim 2, wherein the bonding layer is a solder layer.
 7. The package structure as claimed in claim 2, wherein the bonding layer is an adhesive layer.
 8. The package structure as claimed in claim 2, wherein materials of the pillar and the elongated solder bump are different.
 9. The package structure as claimed in claim 1, wherein an angle between the first horizontal plane and a tangent line of the sidewall surface passing through the upper end of the sidewall surface of the elongated solder bump is in a range from about 60 degrees to about 100 degrees.
 10. The package structure as claimed in claim 1, further comprising: a UBM layer formed between the semiconductor die and the pillar bump; and a conductive element formed between the UBM layer and the pillar bump.
 11. The package structure as claimed in claim 10, wherein the conductive element and the pillar bump are made of the same material.
 12. A package structure, comprising: a semiconductor die; a substrate; a plurality of pillar bumps bonded to the semiconductor die and the substrate; and a plurality of elongated solder bumps bonded to the semiconductor die and the substrate, wherein a height of each of the elongated solder bumps is substantially equal to a height of each of the pillar bumps, wherein each of the elongated solder bumps has a first width, at a first horizontal plane passing through an upper end of a sidewall surface of each of the elongated solder bumps, and a second width, at a second horizontal plane passing through a midpoint of the sidewall surface, and wherein a ratio of the second width to the first width is in a range from about 0.5 to about 1.1.
 13. The package structure as claimed in claim 12, wherein at least some of the elongated solder bumps are formed on first regions of the semiconductor die, at least some of the pillar bumps are formed on second regions of the semiconductor die, and the first regions suffer from stresses higher than those of the second regions.
 14. The package structure as claimed in claim 12, wherein at least some of the elongated solder bumps are formed on corner regions of the semiconductor die.
 15. The package structure as claimed in claim 12, wherein at least some of the elongated solder bumps are formed on both a central region and corner regions of the semiconductor die. 16-20. (canceled)
 21. The package structure as claimed in claim 12, wherein the pillar bumps are conductive.
 22. The package structure as claimed in claim 12, wherein the pillar bump has a sidewall surface substantially perpendicular to a main surface of the semiconductor die.
 23. The package structure as claimed in claim 12, wherein materials of the pillar bumps and the elongated solder bumps are different.
 24. The package structure as claimed in claim 12, wherein an angle between the first horizontal plane and a tangent line of the sidewall surface passing through the upper end of the sidewall surface of one of the elongated solder bumps is in a range from about 60 degrees to about 100 degrees.
 25. The package structure as claimed in claim 12, wherein the second width is greater than the first width. 